Konpozisyon chimik nanASTM B111 C71500 Copper Nikèl Tiyo
| Eleman | % pwa (min) | Pwa % (max) |
|---|---|---|
| Kwiv (Cu) | 65.00 | 70.00 |
| Nikèl (Ni) | 29.00 | 33.00 |
| Fè (Fe) | 0.40 | 1.00 |
| Manganèz (Mn) | - | 1.00 |
| Plon (Pb) | - | 0.02 |
| Zenk (Zn) | - | 0.50 |
| Kabòn (C) | - | 0.05 |
| Fosfò (P) | - | 0.02 |
| Souf (S) | - | 0.02 |
| Lòt (chak) | - | 0.10 |
| Lòt (total) | - | 0.30 |
Pwopriyete mekanik nan C71500 Tib nikèl kwiv san pwoblèm
| Pwopriyete | Valè | Inite |
|---|---|---|
| Fòs rupture | 380 | MPa |
| Fòs rupture | 55 | ksi |
| Fòs Sede (0.5% ekstansyon) | 125 | MPa |
| Fòs Sede (0.5% ekstansyon) | 18 | ksi |
| Elongasyon (nan 2″ oswa 50mm) | 30 | % |
| Rockwell Hardness (HRB) | 75 tipik | - |
| Dite Brinell (HB) | 140 tipik | - |
Valè aktyèl tipik (pa minimòm):
Tensile: 420-480 MPa (61-70 ksi)
Sede: 150-200 MPa (22-29 ksi)
elongasyon: 35-45%
Pwopriyete fizik C71500 Copper Nikèl Alloy Tiyo
| Pwopriyete | Valè | Inite |
|---|---|---|
| Dansite | 8.94 | g/cm³ |
| Dansite | 0.323 | lb/pous³ |
| Pwen fizyon (likid) | 1240 | degre |
| Pwen fizyon (likid) | 2264 | degre F |
| Pwen fizyon (solidis) | 1170 | degre |
| Pwen fizyon (solidis) | 2138 | degre F |
| Kondiktivite tèmik (20 degre) | 29 | W/m·K |
| Kondiktivite tèmik (20 degre) | 17 | BTU/(hr·ft· degre F) |
| Rezistans elektrik (20 degre) | 0.038 | µΩ·m |
| Koefisyan ekspansyon tèmik (20-300 degre) | 16.2 | µm/m·K |
| Koefisyan ekspansyon tèmik (68-572 degre F) | 9.0 | µin/in· degre F |
| Modil Elastisite (Tansyon) | 150 | GPa |
| Modil Elastisite (Tansyon) | 21.8 | 10⁶ psi |
| Kapasite chalè espesifik (20 degre) | 377 | J/kg·K |
| Pèmeyabilite mayetik | <1.01 | - (ki pa-mayetik) |
Tolerans dimansyon pou ASTM B111 C71500 tiyo san pwoblèm
Tolerans dyamèt deyò:
| OD Range | Tolerans (±) |
|---|---|
| Jiska 1″ (25.4 mm) | 0.004″ (0.10 mm) |
| 1″ a 3″ (25.4-76.2 mm) | 0.006″ (0.15 mm) |
| 3″ a 6″ (76.2-152.4 mm) | 0.010″ (0.25 mm) |
Tolerans epesè mi:
| Epesè miray la | Tolerans |
|---|---|
| Tout epesè | ± 10% nan nominal |
Tolerans longè:
| Kalite Longè | Tolerans |
|---|---|
| Longè o aza (estanda 20 pye) | +1/8″ / -0″ |
| Koupe longè (kòmande) | +1/8″ / -0″ |
| Tib mawonnen | Pa akò |
Opsyon epesè mi pou tiyo nikèl kwiv C71500 (BWG pou pous/mm)
| BWG No. | Pous | mm | Aplikasyon tipik |
|---|---|---|---|
| 10 BWG | 0.134 | 3.40 | Devwa lou, presyon ki wo |
| 11 BWG | 0.120 | 3.05 | Dlo lanmè segondè presyon |
| 12 BWG | 0.109 | 2.77 | estanda miray lou |
| 13 BWG | 0.095 | 2.41 | Ki pi komen pou echanjeur chalè |
| 14 BWG | 0.083 | 2.11 | Jeneral kanalizasyon maren |
| 15 BWG | 0.072 | 1.83 | Devwa limyè |
| 16 BWG | 0.065 | 1.65 | Presyon ba sèlman |
| 18 BWG | 0.049 | 1.24 | Pa pou dlo lanmè |
Schedule equivalents for larger diameters (>3″ OD):
| Orè | Epesè miray (4″ tiyo) | Itilizasyon tipik |
|---|---|---|
| SCH 10 | 0.120″ (3.05 mm) | Ba presyon |
| SCH 40 | 0.226″ (5.74 mm) | Presyon estanda |
| SCH 80 | 0.318″ (8.08 mm) | Segondè presyon |
Disponib Gwosè Range pou C71500 san pwoblèm Copper Nikèl Tiyo
| OD Range | Opsyon mi yo | Max Longè |
|---|---|---|
| 1/8″ pou 1″ | 14, 13, 12 BWG | 65 pye |
| 1″ a 3″ | 14, 13, 12, 11, 10 BWG | 40 pye |
| 3″ a 6″ | 12, 11, 10 BWG, SCH 10/40 | 40 pye |
| 6″ a 12″ | SCH 10, 40, 80 | 40 pye |
Tiyo soude (ASTM B111 - gwo dyamèt):
| OD Range | Opsyon mi yo | Max Longè |
|---|---|---|
| 6″ a 24″ | SCH 10, 40, 80 | 40 pye |
Espesifikasyon aplikab ak estanda pou C71500 Copper Nikèl Tiyo
| Estanda | Deskripsyon |
|---|---|
| ASTM B111 | Espesifikasyon estanda pou tib kondansateur san pwoblèm kwiv ak alyaj kwiv |
| ASME SB111 | Menm jan ak ASTM B111, pou aplikasyon pou kòd ASME |
| ASTM B359 | Tib alèt (si sa aplikab) |
| EN 12451 | Estanda Ewopeyen an - CuNi30Mn1Fe |
| BS 2871 CN102 | Britanik estanda (eritaj) - 70/30 nikèl kwiv |
| NACE MR0175 | Pou sèvis tounen (tcheke kondisyon espesifik) |
FAQ
Q1: Ki fòs aktyèl la rupture nan tiyo C71500, pa sèlman minimòm lan?
Tipikman 420-480 MPa (61-70 ksi).Mwayèn moulen nou an se 450 MPa. Minimòm se 380 MPa pou chak ASTM B111.
Q2: Èske tiyo C71500 satisfè NACE MR0175 pou sèvis tounen?
Wi, men tcheke kondisyon espesifik yo.C71500 jeneralman aksepte pou sèvis tounen jiska sèten presyon pasyèl H₂S. Mande sètifikasyon NACE nou an si sa nesesè.
Q3: Ki tolerans epesè miray la sou yon tiyo 13 BWG?
±10% nan 0.095″=±0.0095″.Minimòm miray akseptab se 0.0855″. Maksimòm se 0.1045″.
Q4: Èske ou ka bay yon rapò tès moulen sètifye ak rezilta chimi aktyèl ak rupture?
Wi, pou chak nimewo chalè.Nou imèl analize MTR anvan chajman. Li montre rezilta tès aktyèl yo, pa sèlman minimòm.
Q5: Ki dansite C71500 an lb/in³ pou kalkil pwa?
0.323 lb/pous³.Miltipliye volim tiyo (in³) pa 0.323 pou jwenn pwa an liv.
Q6: Èske C71500 mayetik?
No, pèmeyabilite mayetik se mwens pase 1.01.Si tiyo ou mayetik, li pa C71500 - petèt kontaminasyon an fè oswa alyaj mal.
Q7: Konbyen tan C71500 dire pase C70600 nan dlo lanmè?
Tou depan de kondisyon, 5-15 ane ankò.C71500 gen pi wo kontni nikèl (30% vs 10%) ak pi bon rezistans korozyon, espesyalman nan pi gwo vitès ak tanperati.
Q8: Ki presyon maksimòm pou 1 "13 BWG C71500 tiyo?
Depann sou tanperati.Nan 50 degre, apeprè 2,500 psi presyon k ap travay. Nan 100 degre, diminye a apeprè 1,800 psi. Sèvi ak ASME B31.1 oswa B31.3 pou kalkil egzak.
Q9: Èske ou stock gwosè metrik (OD an mm) pou tiyo C71500?
Wi, pou lòd ekspòtasyon.OD metrik komen: 19.05mm (3/4″ ekivalan), 25.4mm (1″), 50.8mm (2″), 101.6mm (4″). Di nou OD ki nesesè ou ak miray la an mm.
Q10: Èske ou ka pwodwi tiyo C71500 ak sètifikasyon EN 12451 CuNi30Mn1Fe?
Wi, men anplis pri ak tan plon ki pi long.Nou pwodwi ASTM B111 epi bay MTR. Pou sètifikasyon EN 12451, nou travay ak yon twazyèm pati enspektè pou bay sètifika konfòmite.